Plasma Niobium Surface Alloying of P

Plasma Niobium Surface Alloying of Pure Titanium and its Oxidation at 900 ℃

A niobium-modified layer on pure titanium surface was obtained by means of double glow plasma surface alloying technique. The modified layer was uniform, continuous, compact and well adhered to the substrate. The niobium composition in the modified layer decreased gradually from the surface to the substrate. The oxidation behavior of the niobium-modified layer was investigated and compared with the untreated surface at 900 ℃ for 100 h. Characterization of the layers was performed using X-ray diffraction and scanning electron microscope, respectively. The test results show that the oxidation behavior of pure titanium was improved by niobium alloying process. Niobium has a positive influence on the oxidation resistance.

作 者： WANG Wen-bo ZHONG Xu HE Zhi-yong WANG Zhen-xia ZHANG Ping-ze   作者单位： WANG Wen-bo,HE Zhi-yong,WANG Zhen-xia(Research Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan 030024, China)

ZHONG Xu,ZHANG Ping-ze(Research Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan 030024, China;Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China) 

刊 名： 中国航空学报(英文版)  ISTIC 英文刊名： CHINESE JOURNAL OF AERONAUTICS  年，卷(期)： 2007 20(2)  分类号： V2  关键词： niobium   pure titanium   plasma surface alloying   oxidation  

【Plasma Niobium Surface Alloying of P】相关文章：

论可以P与可以不P的关系04-27

学科术语 P05-04

Lead adsorption capacities of different components in natural surface coatings04-26

Changes of plasma membrane ATPase activity,membrane potential and transmembrane proton gradient in Kandelia candel and A04-25

p2p业务员工作计划01-07

p2p理财培训心得体会05-17

神奇的Surface-pen-写物作文600字04-24

LALA的美容心得贴P573-P577(8.2+)04-25

p2p理财培训心得体会6篇05-17

Assessment of Cu, Pb and Hg Contamination in Bottom Sediments Of Surface Water in XuZhou04-26